Manopox 372
Two-component epoxy compound for impregnating carbon fabrics
PRICE
PRICE ON REQUEST
Leave a request — we will send a tailored commercial offer within 30 minutes
Manopox 372 — is two-component epoxy compound for impregnation carbon fabrics. Does not contain solvents. Has long-term pot life and does not have unpleasant odor. Can thicken and be applied as priming and protection layer, depending from requirements project.
✓Manopox 372 in combination with carbon fabrics is systems damp («wet») application for structural strengthening elements structures, in which are expected tensile force. Epoxy impregnation compound recommended for strengthening bridges, elements buildings and other structures in including complex configurations.
✓Strengthening structures is used in cases:
✓Increasing service loads (change design scheme, increase loads, change specified of use);
✓Damage load-bearing elements (corrosion reinforcement, leaching and other damage concrete);
✓Change requirements operation structures (reduction width opening cracks, reduction stress in reinforcement, limitation deformation etc.);
✓Correction errors design or construction (deficiencies section reinforcement or form concrete etc.).
✓Increase resistance dynamic exposures, in including all nature.
✓Excellent mechanical properties;
✓Long-term pot life;
✓High coefficient elongation;
✓Setting in conditions external environment;
✓Contains no solvents.
WEIGHT, KG — AND12,0
WEIGHT, KG — B4,0
COLOR — ANDTransparent
COLOR — BTransparent
TIME APPLICATION AT 20-25°C, MIN60
POT LIFE AT 20-25°C, H4-6
VISCOSITY MIX AT 20-25°C, CP600-700
TEMPERATURE GLASS TRANSITION (TONSG), °C82
STRENGTH LIMIT AT TENSION, MPA50,0
ELASTIC MODULUS AT TENSION, GPA3,2
ELONGATION AT BREAK, %5
BOND STRENGTH WITH CONCRETE, 48 HOURS, MPA>3
STRENGTH LIMIT AT COMPRESSION, MPA86,2
ELASTIC MODULUS AT COMPRESSION, GPA3,2
STRENGTH LIMIT AT BENDING, MPA123,4
ELASTIC MODULUS AT BENDING, GPA3,1