Manopur 336
Three-component polyurethane compound for forming the pre-joint zone
PRICE
PRICE ON REQUEST
Leave a request — we will send a tailored commercial offer within 30 minutes
Manopur 336 - three-component polyurethane resin for filling transition zones movement, and also other type joints, exposed permanent dynamic loads. After curing compound forms strong elastic material, resistant to exposure to UV radiation and reagents. Has high wear-resistant. Thanks to its own characteristics Manopur 336 reliable seals space between asphalt concrete coatings and metal profile movement joint, compensating arising deformation, vibration, shear and impact loads.
✓Filling transition joints movement and other type joints at construction vehicles roads, iron roads, and also airfields;
✓Restoration geometry concrete and reinforced concrete structures, exposed permanent dynamic loads;
✓Fixing railway sleepers;
✓Installation leveling layer at installation equipment, providing vibration exposure.
✓Reduction impact exposure, vibration and level noise, caused transport agents and equipment;
✓Uniform redistribution loads on structure;
✓Resistance to abrasion, High Strength on shear and tensile failure;
✓Method withstand deformation with retention water tightness;
✓Excellent resistance to action of aggressive environments: petroleum products, reagents, mineral oils, wastewater water, thinning acids and alkalis;
✓High frost resistance, resistance to action of ozone and UV radiation;
✓High mechanical characteristics in wide interval temperatures;
✓Fast commissioning;
✓High adhesion to concrete and metal surfaces;
✓Ease installation, easy treatment placed material.
COLORBlack
MIXING RATIO A : B1 : B2, PARTS BY WEIGHT25 : 3 : 2
POT LIFE, NOT LESS THAN, MIN, AT 23°C10
TIME TO RETURN TO SERVICE, H, AT 20°C — PASSENGER-CAR TRAFFIC6-8
TIME TO RETURN TO SERVICE, H, AT 20°C — TRAFFIC TRUCKS TRANSPORT24
TIME FULL CURING, DAYS7
MINIMUM / MAXIMUM AIR TEMPERATURE AND SURFACE AT INSTALLATION, °C+5 / +35
CONSUMPTION, KG/LITERS2,1
COMPRESSIVE STRENGTH, MPA, 7 DAYS, NOT LESS THAN20
TENSILE STRENGTH AT BENDING, MPA, 7 DAYS, NOT LESS THAN13
BOND STRENGTH WITH CONCRETE SUBSTRATE, MPA, NOT LESS THAN3,5
BOND STRENGTH WITH METAL SUBSTRATE, MPA, NOT LESS THAN5,5
WATER BY BY WEIGHT, %0,1