WATERPROOFING
Starmex 111
Cement-based waterproof coating for concrete and masonry structures
PRICE
PRICE ON REQUEST
Leave a request — we will send a tailored commercial offer within 30 minutes
Starmex 111 — dry mix based on cement, forms waterproofing coating with high waterproof and adhesion to mineral surfaces.
✓Vertical and horizontal waterproofing new and existing structures from concrete and reinforced concrete;
✓Waterproofing wet rooms, buried structures, tunnels, under walls, slabs floor slabs, reservoirs, silos, treatment structures, wells and etc.
✓Water tightness at positive and negative hydrostatic pressure;
✓Vapor permeability;
✓Application on damp substrate;
✓Increase frost resistance substrate;
✓Increases chemical resistance concrete and has corrosion protection properties;
✓Does not contain years organic substances, environmental without. Permitted contact with drinking water;
✓Application machine method.
✓Possible application brush.
MAXIMUM AGGREGATE SIZE AGGREGATE, MM≤0,63
CONTENT GRAINS MAXIMUM SIZE, %≤5,0
BULK DENSITY, KG/M³1250±100
QUANTITY LIQUID FOR MIXING (MANOCRYL SETMIX + WATER FOR PREPARATION MIX), %26,5±1,5
MASS RATIO MANOCRYL SETMIX: WATER FOR PREPARATION MIX, WT. H.1:3
DENSITY MORTAR MIX, KG/M³2000±200
FLOWABILITY MIX BY FLOW SPREAD CONE ON VIBRATING TABLE, MM230±20
SHELF LIFE INITIAL MOBILITY, MIN≥40
TENSILE STRENGTH AT BENDING, 28 DAYS, MPA≥4,5
COMPRESSIVE STRENGTH, 28 DAYS, MPA≥35
BOND STRENGTH WITH CONCRETE SUBSTRATE, 28 DAYS, MPA≥1,5
GRADE BY WATER TIGHTNESSNot below W12
GRADE BY FROST RESISTANCE>F200
PROCESS INTERVAL TO RETURN TO SERVICE, DAYS7
MINIMUM APPLICATION TEMPERATURE, °C+5