Starmex Flex Express
Elastic polymer-cement waterproofing coating with accelerated return to service
PRICE
PRICE ON REQUEST
Leave a request — we will send a tailored commercial offer within 30 minutes
Starmex Flex Express — elastic wear-resistant waterproofing coating with high adhesion to mineral and metal surfaces and shortened time return to service. Material has method bridge cracks. Coating is abrasion-resistant and chemical resistance to action of corrosion liquids, such as thinning acids and alkalis. Has good UV-resistance.
✓Waterproofing structures, exposed action of mechanical loads with possible formation cracks, for example, terraces and balconies;
✓Waterproofing and protection concrete surfaces, accessible for maintenance, for example, reservoirs water, swimming pools, showers, wet rooms;
✓Installation waterproofing with fast period return to service (shortened time holding time coating to contact with liquid environment, in including at hydrostatic pressure).
✓Fast commissioning;
✓High water tightness;
✓Vapor permeability;
✓Application on damp substrate;
✓Elasticity, method bridge cracks;
✓Wear resistance;
✓Good chemical resistance and corrosion protection properties;
✓Reduction time curing in heat at performing work in winter period by comparison with conventional polymer waterproofing compound.
MAXIMUM AGGREGATE SIZE AGGREGATE, MM≤0,63
CONTENT GRAINS MAXIMUM SIZE, %≤5,0
BULK DENSITY, KG/M³1400 ±100
DENSITY AT 20°C, KG/M³1050±70
DENSITY MORTAR MIX, KG/M³1700±200
FLOWABILITY MIX BY FLOW SPREAD CONE ON VIBRATING TABLE, MM250±20
SHELF LIFE INITIAL MOBILITY, MIN≥40
TENSILE STRENGTH, MPA1,5
ELONGATION, %≥60
BOND STRENGTH WITH CONCRETE SUBSTRATE, MPA≥1,2
BOND STRENGTH WITH METAL SUBSTRATE, MPA0,8
GRADE BY WATER TIGHTNESSNot below W12
CRACKS COATING ON CONCRETE, MM≥1,5
PROCESS INTERVAL BETWEEN COATS, HOURS1...4
MINIMUM APPLICATION TEMPERATURE, °C+5